Injection molding (British English: moulding) is a manufacturing process for producing parts from both thermoplastic and thermosetting plastic materials. Material is fed into a heated barrel, mixed, and forced into a mold cavity where it cools and hardens to the configuration of the mold cavity. ^[1] After a product is designed, usually by an industrial designer or an engineer, molds are made by a moldmaker (or toolmaker) from metal, usually either steel or aluminium, and precision-machined to form the features of the desired part. Injection molding is widely used for manufacturing a variety of parts, from the smallest component to entire body panels of cars.

Contents 1 Process Characteristics 2 History 3 Applications 4 Examples of Polymers Best Suited for the Process 5 Design Considerations for the Process 6 Equipment 6.1 Mold 6.2 Mold Design 6.3 Effects on the material properties 6.4 Tool Materials 6.5 Geometrical Possibilities 6.6 Machining 6.7 Cost 7 Injection process 7.1 Injection Molding Cycle 7.2 Time Function 7.3 Different types of injection molding processes 8 Process Troubleshooting 8.1 Molding trial 8.2 Molding defects 8.3 Tolerances and Surfaces 9 Lubrication and Cooling 10 Power Requirements 11 Inserts 12 Gallery 13 See also 14 Notes 15 References 16 External links

[edit] Process Characteristics

• Utilizes a ram or screw-type plunger to force molten plastic material into a mold cavity
• Produces a solid or open-ended shape which has conformed to the contour of the mold
• Uses thermoplastic or thermoset materials
• Produces a parting line, sprue, and gate marks
• Ejector pin marks are usually present

^[2]

[edit] History

The first man-made plastic was invented in Britain in 1851 by Alexander Parkes. He publicly demonstrated it at the 1862 International Exhibition in London, calling the material he produced "Parkesine." Derived from cellulose, Parkesine could be heated, molded, and retain its shape when cooled. It was, however, expensive to produce, prone to cracking, and highly flammable.

In 1868, American inventor John Wesley Hyatt developed a plastic material he named Celluloid, improving on Parkes' invention so that it could be processed into finished form. Together with his brother Isaiah, Hyatt patented the first injection molding machine in 1872.^[3] This machine was relatively simple compared to machines in use today. It worked like a large hypodermic needle, using a plunger to inject plastic through a heated cylinder into a mold. The industry progressed slowly over the years, producing products such as collar stays, buttons, and hair combs.

The industry expanded rapidly in the 1940s because World War II created a huge demand for inexpensive, mass-produced products. In 1946, American inventor James Watson Hendry built the first screw injection machine, which allowed much more precise control over the speed of injection and the quality of articles produced. This machine also allowed material to be mixed before injection, so that colored or recycled plastic could be added to virgin material and mixed thoroughly before being injected. Today screw injection machines account for the vast majority of all injection machines. In the 1970s, Hendry went on to develop the first gas-assisted injection molding process, which permitted the production of complex, hollow articles that cooled quickly. This greatly improved design flexibility as well as the strength and finish of manufactured parts while reducing production time, cost, weight and waste.

The plastic injection molding industry has evolved over the years from producing combs and buttons to producing a vast array of products for many industries including automotive, medical, aerospace, consumer products, toys, plumbing, packaging, and construction.^[4]

[edit] Applications

Injection molding is used to create many things such as milk cartons, packaging, bottle caps, automotive dashboards, pocket combs, and most other plastic products available today. Injection molding is the most common method of part manufacturing. It is ideal for producing high volumes of the same object.^[5] Some advantages of injection molding are high production rates, repeatable high tolerances, the ability to use a wide range of materials, low labour cost, minimal scrap losses, and little need to finish parts after molding. Some disadvantages of this process are expensive equipment investment, potentially high running costs, and the need to design moldable parts.^[6]

[edit] Examples of Polymers Best Suited for the Process

Most polymers may be used, including all thermoplastics, some thermosets, and some elastomers.^[7] In 1995 there were approximately 18,000 different materials available for injection molding and that number was increasing at an average rate of 750 per year. The available materials are alloys or blends of previously developed materials meaning that product designers can choose from a vast selection of materials, one that has exactly the right properties. Materials are chosen based on the strength and function required for the final part but also each material has different parameters for molding that must be taken into account.^[8] Common polymers like Epoxy and phenolic are examples of thermosetting plastics while nylon, polyethylene, and polystyrene are thermoplastic.^[9]

[edit] Design Considerations for the Process

It is important when designing products for injection molding that you consider how they will be formed in the machine, how they will be taken out of the machine, and the structure of the final product. Some important guidelines are:

• Use approximately uniform wall thicknesses throughout your designs.
• Keep walls thin - typically between 1/32" and 1/10". This allows for proper cooling and reduces cost by minimizing use of material. Thin walls also reduce problems with material shrinkage. Although some unevenness will occur due to shrinkage, walls as thick as 1/5" can be used. Keep wall thickness at least wall length / 50. Keep 90 deg walls under 0.25" high. Keep thickness of ejection pin surface wall at least .07".
• To strengthen parts, instead of using thicker walls, use additional structures such as ribs. Use fillets at the base of ribs.
  
• When using a rib make it about half the main wall thickness.
• Round corners and edges wherever possible.
• For easy release of the part from the mold, add a slight taper to the sides (typically ~ 2 deg) - especially for textured walls and walls higher than 0.25".
• Avoid undercuts that are impossible to remove from the mold.
• Lighter colors hide flow patterns better than dark colors.
• Where walls meet at a 90 angle, round inside and outside to at least .05" radius - sharper outside corners can create molding problems and sharper inside corners will increase tooling cost.
• Keep holes at least .015" from edges.^[10]

[edit] Equipment

Injection molding machines consist of a material hopper, an injection ram or screw-type plunger, and a heating unit.^[11] They are also known as presses, they hold the molds in which the components are shaped. Presses are rated by tonnage, which expresses the amount of clamping force that the machine can exert. This force keeps the mold closed during the injection process. Tonnage can vary from less than 5 tons to 6000 tons, with the higher figures used in comparatively few manufacturing operations. The total clamp force needed is determined by the projected area of the part being molded. This projected area is multiplied by a clamp force of from 2 to 8 tons for each square inch of the projected areas. As a rule of thumb, 4 or 5 tons/in² can be used for most products. If the plastic material is very stiff, it will require more injection pressure to fill the mold, thus more clamp tonnage to hold the mold closed.^[12] The required force can also be determined by the material used and the size of the part, larger parts require higher clamping force.^[13]

[edit] Mold

Mold or die are the common terms used to describe the tooling used to produce plastic parts in molding.

Traditionally, molds have been expensive to manufacture. They were usually only used in mass production where thousands of parts were being produced. Molds are typically constructed from hardened steel, pre-hardened steel, aluminium, and/or beryllium-copper alloy. The choice of material to build a mold from is primarily one of economics, steel molds generally cost more to construct, but their longer lifespan will offset the higher initial cost over a higher number of parts made before wearing out. Pre-hardened steel molds are less wear resistant and are used for lower volume requirements or larger components. The steel hardness is typically 38-45 on the Rockwell-C scale. Hardened steel molds are heat treated after machining. These are by far the superior in terms of wear resistance and lifespan. Typical hardness ranges between 50 and 60 Rockwell-C (HRC). Aluminium molds can cost substantially less, and when designed and machined with modern computerized equipment, can be economical for molding tens or even hundreds of thousands of parts. Beryllium copper is used in areas of the mold which require fast heat removal or areas that see the most shear heat generated.^[14] The molds can be manufactured by either CNC machining or by using Electrical Discharge Machining processes

Injection molding die with side pulls

"A" side of die for 25% glass-filled acetal with 2 side pulls.

Close up of removable insert in "A" side.

"B" side of die with side pull actuators.

Insert removed from die.

[edit] Mold Design

The mold consists of two primary components, the injection mold (A plate) and the ejector mold (B plate). Plastic resin enters the mold through a sprue in the injection mold, the sprue bushing is to seal tightly against the nozzle of the injection barrel of the molding machine and to allow molten plastic to flow from the barrel into the mold, also known as cavity^[15] The sprue bushing directs the molten plastic to the cavity images through channels that are machined into the faces of the A and B plates. These channels allow plastic to run along them, so they are referred to as runners.^[16] The molten plastic flows through the runner and enters one or more specialized gates and into the cavity^[17] geometry to form the desired part.

The amount of resin required to fill the sprue, runner and cavities of a mold is a shot. Trapped air in the mold can escape through air vents that are ground into the parting line of the mold. If the trapped air is not allowed to escape, it is compressed by the pressure of the incoming material and is squeezed into the corners of the cavity, where it prevents filling and causes other defects as well. The air can become so compressed that it ignites and burns the surrounding plastic material.^[18] To allow for removal of the molded part from the mold, the mold features must not overhang one another in the direction that the mold opens, unless parts of the mold are designed to move from between such overhangs when the mold opens (utilizing components called Lifters).

Sides of the part that appear parallel with the direction of draw (The axis of the cored position (hole) or insert is parallel to the up and down movement of the mold as it opens and closes)^[19] are typically angled slightly with (draft) to ease release of the part from the mold. Insufficient draft can cause deformation or damage. The draft required for mold release is primarily dependent on the depth of the cavity: the deeper the cavity, the more draft necessary. Shrinkage must also be taken into account when determining the draft required.^[20] If the skin is too thin, then the molded part will tend to shrink onto the cores that form them while cooling, and cling to those cores or part may warp, twist, blister or crack when the cavity is pulled away.^[21] The mold is usually designed so that the molded part reliably remains on the ejector (B) side of the mold when it opens, and draws the runner and the sprue out of the (A) side along with the parts. The part then falls freely when ejected from the (B) side. Tunnel gates, also known as submarine or mold gate, is located below the parting line or mold surface. The opening is machined into the surface of the mold on the parting line. The molded part is cut (by the mold) from the runner system on ejection from the mold.^[22] Ejector pins, also known as knockout pin, is a circular pin placed in either half of the mold (usually the ejector half) which pushes the finished molded product, or runner system out of a mold.^[23]

The standard method of cooling is passing a coolant (usually water) through a series of holes drilled through the mold plates and connected by hoses to form a continueous pathway. The coolant absorbs heat from the mold (which has absorbed heat from the hot plastic) and keeps the mold at a proper temperature to solidify the plastic at the most efficient rate.^[24]

To ease maintenance and venting, cavities and cores are divided into pieces, called inserts, and sub-assemblies, also called inserts, blocks, or chase blocks. By substituting interchangeable inserts, one mold may make several variations of the same part.

More complex parts are formed using more complex molds. These may have sections called slides, that move into a cavity perpendicular to the draw direction, to form overhanging part features. When the mold is opened, the slides are pulled away from the plastic part by using stationary “angle pins” on the stationary mold half. These pins enter a slot in the slides and cause the slides to move backward when the moving half of the mold opens. The part is then ejected and the mold closes. The closing action of the mold causes the slides to move forward along the angle pins.^[25]

Some molds allow previously molded parts to be reinserted to allow a new plastic layer to form around the first part. This is often referred to as overmolding. This system can allow for production of one-piece tires and wheels.

2-shot or multi-shot molds are designed to "overmold" within a single molding cycle and must be processed on specialized injection molding machines with two or more injection units. This process is actually an injection molding process performed twice. In the first step, the base color material is molded into a basic shape. Then the second material is injection-molded into the remaining open spaces. That space is then filled during the second injection step with a material of a different color.^[26]

A mold can produce several copies of the same parts in a single "shot". The number of "impressions" in the mold of that part is often incorrectly referred to as cavitation. A tool with one impression will often be called a single impression(cavity) mold.^[27] A mold with 2 or more cavities of the same parts will likely be referred to as multiple impression (cavity) mold.^[28] Some extremely high production volume molds (like those for bottle caps) can have over 128 cavities.

In some cases multiple cavity tooling will mold a series of different parts in the same tool. Some toolmakers call these molds family molds as all the parts.^[29]

[edit] Effects on the material properties

The mechanical properties of a part are usually little affected. Some parts can have internal stresses in them. This is one of the reasons why it's good to have uniform wall thickness when molding. One of the physical property changes is shrinkage. A permanent chemical property change is the material thermoset, which can't be remelted to be injected again.^[30]

[edit] Tool Materials

Tool steel or beryllium-copper are often used. Mild steel, aluminum, nickel or epoxy are only suitable for prototype or very short production runs.^[31] Modern hard aluminum (7075 and 2024 alloys) with proper mold design, can easily make molds capable of 100,000 or more part life.^{[citation needed]}

[edit] Geometrical Possibilities

The most commonly used plastic molding process, injection molding, is used to create a large variety of products with different shapes and sizes. Most importantly, they can create products with complex geometry that many other processes cannot. There are a few precautions when designing something that will be made using this process to reduce the risk of weak spots. First, streamline your product or keep the thickness relatively uniform. Second, try and keep your product between 2 to 20 inches.

The size of a part will depend on a number of factors (material, wall thickness, shape,process etc). The initial raw material required may be measured in the form of granules, pellets or powders. Here are some ranges of the sizes.

Method	Raw Materials	Maximum Size	Minimum Size
Injection Molding (thermo-plastic)	Granules, Pellets, Powders	700 oz.	Less than 1 oz.
Injection Molding (thermo-setting)	Granules, Pellets, Powders	200 oz.	Less Than 1 oz.

^[32]

[edit] Machining

Molds are built through two main methods: standard machining and EDM. Standard Machining, in its conventional form, has historically been the method of building injection molds. With technological development, CNC machining became the predominant means of making more complex molds with more accurate mold details in less time than traditional methods.

The electrical discharge machining (EDM) or spark erosion process has become widely used in mold making. As well as allowing the formation of shapes which are difficult to machine, the process allows pre-hardened molds to be shaped so that no heat treatment is required. Changes to a hardened mold by conventional drilling and milling normally require annealing to soften the mold, followed by heat treatment to harden it again. EDM is a simple process in which a shaped electrode, usually made of copper or graphite, is very slowly lowered onto the mold surface (over a period of many hours), which is immersed in paraffin oil. A voltage applied between tool and mold causes spark erosion of the mold surface in the inverse shape of the electrode.^[33]

[edit] Cost

The cost of manufacturing molds depends on a very large set of factors ranging from number of cavities, size of the parts (and therefore the mold), complexity of the pieces, expected tool longevity, surface finishes and many others. The initial cost is great, however the piece part cost is low, so with greater quantities the overall price decreases.

[edit] Injection process

With Injection Molding, granular plastic is fed by gravity from a hopper into a heated barrel. As the granules are slowly moved forward by a screw-type plunger, the plastic is forced into a heated chamber, where it is melted. As the plunger advances, the melted plastic is forced through a nozzle that rests against the mold, allowing it to enter the mold cavity through a gate and runner system. The mold remains cold so the plastic solidifies almost as soon as the mold is filled.^[34]

[edit] Injection Molding Cycle

The sequence of events during the injection mold of a plastic part is called the injection molding cycle. The cycle begins when the mold closes, followed by the injection of the polymer into the mold cavity. Once the cavity is filled, a holding pressure is maintained to compensate for material shrinkage. In the next step, the screw turns, feeding the next shot to the front screw.This causes the screw to retract as the next shot is prepared. Once the part is sufficiently cool, the mold opens and the part is ejected. ^[35]

[edit] Time Function

The time it takes to make a product using injection molding can be calculated by adding: Twice the Mold Open/Close Time (2M) + Injection Time (T) + Cooling Time (C) + Ejection Time (E) Where T is found by dividing: Mold Size (S) / Flow Rate (F) Total time = 2M + T + C + E T = V/R V = Mold cavity size (in3) R = Material flow rate (in3/min)

^[36]

The total cycle time can be calculated using t_cycle = t_closing + t_cooling + t_ejection^[37]

• The closing and ejection times, can last from a fraction of a second to a few seconds, depending on the size of the mold and machine. The cooling times, which dominate the process, depend on the maximum thickness of the part.^[38]

[edit] Different types of injection molding processes

Although most injection molding processes are covered by the conventional process description above, there are several important molding variations including:

• Co-injection (sandwich) molding
• Fusible (lost, soluble) core injection molding
• Gas-assisted injection molding
• In-mold decoration and in mold lamination
• Injection-compression molding
• Insert and outsert molding
• Lamellar (microlayer) injection molding
• Low-pressure injection molding
• Microinjection molding
• Microcellular molding
• Multicomponent injection molding (overmolding)
• Multiple live-feed injection molding
• Powder injection molding
• Push-Pull injection molding
• Reaction injection molding
• Resin transfer molding
• Rheomolding
• Structural foam injection molding
• Structural reaction injection molding
• Thin-wall molding
• Vibration gas injection molding
• Water assisted injection molding
• Rubber injection
• Injection molding of liquid silicone rubber^[39]

For more details about the different types injection processes.[1]

[edit] Process Troubleshooting

Optimal process settings are critical to influencing the cost, quality, and productivity of plastic injection molding. The main trouble in injection molding is to have a box of good plastics parts contaminated with scrap. For that reason process optimization studies have to be done and process monitoring has to take place. To have a constant filling rate in the cavity the switch over from injection phase to the holding phase can be made based on a cavity pressure level.
Having a stable production window the following issues are worth to investigate:
The Metering phase can be optimized by varying screw turns per minute and backpressure. Variation of time needed to reload the screw gives an indication of the stability of this phase.
Injection speed can be optimized by pressure drop studies between pressure measured in the Nozzle (alternatively hydraulic pressure) and pressure measured in the cavity. Melted material with a lower viscosity has less pressure loss from nozzle to cavity than material with a higher viscosity. Varying the Injection speed changes the sheer rate. Higher speed = higher sheer rate = lower viscosity. Pay attention increasing the mold and melt temperature lowers the viscosity but lowers the sheer rate too.
Gate seal or gate freeze / sink mark / weight and geometry studies have the approach to prevent sink marks and geometrical faults. Optimizing the high and duration of applied holding pressure based on cavity pressure curves is the appropriate way to go. The thicker the part the longer the holding pressure applied. The thinner the part the shorter the holding pressure applied.
Cooling time starts once the injection phase is finished. The hotter the melted plastics the longer the cooling time the thicker the part produced the longer the cooling time.

[edit] Molding trial

When filling a new or unfamiliar mold for the first time, where shot size for that mold is unknown, a technician/tool setter usually starts with a small shot weight and fills gradually until the mold is 95 to 99% full. Once this is achieved a small amount of holding pressure will be applied and holding time increased until gate freeze off (solidification time) has occurred. Gate solidification time is an important as it determines cycle time, which itself is an important issue in the economics of the production process.^[40] Holding pressure is increased until the parts are free of sinks and part weight has been achieved. Once the parts are good enough and have passed any specific criteria, a setting sheet is produced for people to follow in the future. The method to setup an unknown mold the first time can be supported by installing cavity pressure sensors. To see how much the cavities are filled the pressure in the cavity gives a good indication for. Once the mold is set up the first time modern monitoring systems can save a reference curve of the cavity pressure. With that it is possible to reproduce the same part quality on another molding machine within a short setup time.

[edit] Molding defects

Injection molding is a complex technology with possible production problems. They can either be caused by defects in the molds or more often by part processing (molding)

Molding Defects	Alternative name	Descriptions	Causes
Blister	Blistering	Raised or layered zone on surface of the part	Tool or material is too hot, often caused by a lack of cooling around the tool or a faulty heater
Burn marks	Air Burn/ Gas Burn/ Dieseling	Black or brown burnt areas on the part located at furthest points from gate or where air is trapped	Tool lacks venting, injection speed is too high
Color streaks (US)	Colour streaks (UK)	Localized change of color/colour	Masterbatch isn't mixing properly, or the material has run out and it's starting to come through as natural only. Previous colored material "dragging" in nozzle or check valve.
Delamination		Thin mica like layers formed in part wall	Contamination of the material e.g. PP mixed with ABS, very dangerous if the part is being used for a safety critical application as the material has very little strength when delaminated as the materials cannot bond
Flash	Burrs	Excess material in thin layer exceeding normal part geometry	Mold is over packed or parting line on the tool is damaged, too much injection speed/material injected, clamping force too low. Can also be caused by dirt and contaminants around tooling surfaces.
Embedded contaminates	Embedded particulates	Foreign particle (burnt material or other) embedded in the part	Particles on the tool surface, contaminated material or foreign debris in the barrel, or too much shear heat burning the material prior to injection
Flow marks	Flow lines	Directionally "off tone" wavy lines or patterns	Injection speeds too slow (the plastic has cooled down too much during injection, injection speeds must be set as fast as you can get away with at all times)
Jetting		Deformed part by turbulent flow of material	Poor tool design, gate position or runner. Injection speed set too high.
Knit Lines	Weld lines	Small lines on the backside of core pins or windows in parts that look like just lines.	Caused by the melt-front flowing around an object standing proud in a plastic part as well as at the end of fill where the melt-front comes together again. Can be minimized or eliminated with a mold-flow study when the mold is in design phase. Once the mold is made and the gate is placed one can only minimize this flaw by changing the melt and the mold temperature.
Polymer degradation		polymer breakdown from hydrolysis, oxidation etc	Excess water in the granules, excessive temperatures in barrel
Sink marks	[sinks]	Localized depression (In thicker zones)	Holding time/pressure too low, cooling time too short, with sprueless hot runners this can also be caused by the gate temperature being set too high. Excessive material or thick wall thickness.
Short shot	Non-fill / Short mold	Partial part	Lack of material, injection speed or pressure too low, mold too cold
Splay marks	Splash mark / Silver streaks	Circular pattern around gate caused by hot gas	Moisture in the material, usually when hygroscopic resins are dried improperly. Trapping of gas in "rib" areas due to excessive injection velocity in these areas. Material too hot.
Stringiness	Stringing	String like remain from previous shot transfer in new shot	Nozzle temperature too high. Gate hasn't frozen off
Voids		Empty space within part (Air pocket)	Lack of holding pressure (holding pressure is used to pack out the part during the holding time). Also mold may be out of registration (when the two halves don't center properly and part walls are not the same thickness).
Weld line	Knit line / Meld line / Transfer line	Discolored line where two flow fronts meet	Mold/material temperatures set too low (the material is cold when they meet, so they don't bond). Point between injection and transfer (to packing and holding) too early.
Warping	Twisting	Distorted part	Cooling is too short, material is too hot, lack of cooling around the tool, incorrect water temperatures (the parts bow inwards towards the hot side of the tool)

[edit] Tolerances and Surfaces

Molding tolerance is a specified allowance on the deviation in parameters such as dimensions, weights, shapes, or angles, etc. To maximize control in setting tolerances there is usually a minimum and maximum limit on thickness, based on the process used.^[41] Injection molding typically is capable of tolerances equivalent to an IT Grade of about 9–14. The possible tolerance of a thermoplastic or a thermoset is ±0.008 to ±0.002 inches. Surface finishes of two to four microinches or better are can be obtained. Rough or pebbled surfaces are also possible.

Molding Type	Typical	Possible
Thermoplastic	±0.008	±0.002
Thermoset	±0.008	±0.002

[edit] Lubrication and Cooling

Obviously, the mold must be cooled in order for the production to take place. Because of the heat capacity, inexpensiveness, and availability of water, water is used as the primary cooling agent. To cool the mold, water can be channeled through the mold to account for quick cooling times. Usually a colder mold is more efficient because this allows for faster cycle times. However, this is not always true because crystalline materials require the opposite of a warmer mold and lengthier cycle time. ^[42]

[edit] Power Requirements

The power required for this process of injection molding depends on many things and varies between materials used. Manufacturing Processes Reference Guide states that the power requirements depend on "a material's specific gravity, melting point, thermal conductivity, part size, and molding rate." Below is a table from page 243 of the same reference as previously mentioned which best illustrates the characteristics relevant to the power required for the most commonly used materials.

Material	Specific Gravity	Melting Point (°F)
Epoxy	1.12 to 1.24	248
Phenolic	1.34 to 1.95	248
Nylon	1.01 to 1.15	381 to 509
Polyethylene	0.91 to 0.965	230 to 243
Polystyrene	1.04 to 1.07	338

[edit] Inserts

Metal inserts can be also be injection molded into the workpiece. For large volume parts the inserts are placed in the mold using automated machinery. An advantage of using automated components is that the smaller size of parts allows a mobile inspection system that can be used to examine multiple parts in a decreased amount of time. In addition to mounting inspection systems on automated components, multiple axial robots are also capable of removing parts from the mold and place them in latter systems that can be used to ensure quality of multiple parameters. The ability of automated components to decrease the cycle time of the processes allows for a greater output of quality parts.^[43]

Specific instances of this increased efficiency include the removal of parts from the mold immediately after the parts are created and use in conjunction with vision systems. The removal of parts is achieved by using robots to grip the part once it has become free from the mold after in ejector pins have been raised. The robot then moves these parts into either a holding location or directly onto an inspection system, depending on the type of product and the general layout of the rest of the manufacturer's production facility. Visions systems mounted on robots are also an advancement that has greatly changed the way that quality control is performed in insert molded parts. A mobile robot is able to more precisely determine the accuracy of the metal component and inspect more locations in the same amount of time as a human inspector.^[43]

[edit] Gallery

Lego injection mold, lower side

Lego injection mold, detail of lower side

Lego injection mold, upper side

Lego injection mold, detail of upper side

[edit] See also

• Reaction injection molding, a similar technique to standard injection molding, enables the use of thermoset polymers to produce large and complex parts.
• Liquid injection molding, a process that involves an integrated system for proportioning, mixing, and dispensing dual-component liquid resin formulations and directly injecting the resultant mix into a mold which is clamped under pressure.
• Hobby injection molding
• Fusible core injection molding

[edit] Notes

[edit] References

• Bryce, Douglas M. Plastic Injection Molding: Manufacturing Process Fundamentals. SME, 1996.
• Brydson, J, Plastics Materials, Butterworths 9th Ed (1999).
• Callister, William D, Materials Science and Engineering: An Introduction, John Wiley and Sons
• Lewis, Peter Rhys, Reynolds, K, Gagg, C, Forensic Materials Engineering: Case studies, CRC Press (2004).
• Osswald, Tim A; Lih-Sheng Turng, Paul J.Gramamn. Injection Molding Handbook 2nd Ed. Hanser Verlag., 2007
• Osswald, Tim A. International Plastics Handbook. Hanser Verlag., 2006
• Rosato, Donald V; Marlene G. Rosato. Concise Encyclopedia of Plastics. Springer, 2000.
• Rosato, Dominick; Rosato Marlene, and Rosato Donald Injection Molding Handbook 3rd Ed. Kluwer Academic Publishers, 2000.
• Todd, Robert H; Dell K. Allen and Leo Alting Manufacturing Processes Reference Guide. Industrial Press Inc., 1994. pgs. 240-245
• Whelan, Tony. Polymer Technology Dictionary Springer, 1994.

[edit] External links

• Injection molding cost estimator
• Injection molding cost estimator (detailed)
• Injection molding machine states
• Shrinkage & warpage
• Injection molding interactive animation
• Injection molding guidelines