Representative curves of applied stress vs number of cycles for steel (in blue and showing an endurance limit) and aluminium (in red and showing no such limit).

Fatigue limit, endurance limit, and fatigue strength are all expressions used to describe a property of materials: the amplitude (or range) of cyclic stress that can be applied to the material without causing fatigue failure.^[1] Ferrous alloys and titanium alloys ^[2] have a distinct limit, an amplitude below which there appears to be no number of cycles that will cause failure. Other structural metals such as aluminium and copper, do not have a distinct limit and will eventually fail even from small stress amplitudes. In these cases, a number of cycles (usually 10⁷) is chosen to represent the fatigue life of the material.

[edit] Definitions

The ASTM defines fatigue strength, S_Nf, as the value of stress at which failure occurs after N_f cycles, and fatigue limit, S_f, as the limiting value of stress at which failure occurs as N_f becomes very large. ASTM does not define endurance limit but implies that it is similar to fatigue limit.^[3]

Some authors use endurance limit, S_e, for the stress below which failure never occurs, even for an indefinitely large number of loading cycles, as in the case of steel; and fatigue limit or fatigue strength, S_f, for the stress at which failure occurs after a specified number of loading cycles, such as 500 million, as in the case of aluminium.^[1][4][5] Other authors do not differentiate between the expressions even if they do differentiate between the two types of materials.^[6][7][8]

[edit] Typical values

Typical values of the limit (S_e) for steels are 1/2 the ultimate tensile strength, to a maximum of 100 ksi (690 MPa). For iron, aluminium, and copper alloys, S_e is typically 0.4 times the ultimate tensile strength. Maximum typical values for irons are 24 ksi (165 MPa), aluminums 19 ksi (131 MPa), and coppers 14 ksi (96.5 MPa).^[2]

[edit] History

The concept of endurance limit was introduced in 1870 by August Wöhler.^[9] However, recent research suggests that endurance limits do not actually exist, that if enough stress cycles are performed, even the smallest stress will eventually produce fatigue failure.^[5][10]